Project location: Thailand

Product: Blast Joint

1. Blast Joint 3.063" OD x 1.610" ID x 18.00" OAL

　　250Ra OD 64Ra ID

　Grade : AISI 4140-80K

　Quantity: 2 pieces

2. Blast Joint 2.350" OD x 1.6" ID x 6FT

　　250Ra OD 64Ra ID

　Grade : AISI 4140-80K

　Quantity: 4 pieces

3. Blast Joint 2.350" OD x 1.6" ID x 10FT

　　250Ra OD 64Ra ID

　Grade : AISI 4140-110K

　Quantity: 4 pieces

1. Blast Joint 4140-80K

　Chemical composition：

C	Si	Mn	P	S	Cr	Ni	Mo	Cu	Al	V	Nb	Ti	Di(inch)
0.41	0.23	0.95	0.009	0.003	1.05	0.18	0.22	0.10	0.030	0.008	0.002	0.0065	6.34

　Mechanical Properties：

Yield Strength(Mpa)	Tensile Strength(Mpa)	Elongation A(%)	Reduction Z(%)
595	728	27	66

2. Blast Joint 4140-110K

　Chemical composition：

C	Si	Mn	P	S	Cr	Ni	Mo	Cu	Al	V	B
0.44	0.24	0.98	0.010	0.003	1.07	0.18	0.22	0.12	0.023	0.008	0.0003

　Mechanical Properties：

Yield Strength(Mpa)	Tensile Strength(Mpa)	Elongation A(%)	Reduction Z(%)
933	1047	19	57

　　ETANG has just successfully delivered a batch of blast joint to a long-standing customer in Thailand. All delivered products have been processed, heat-treated, and surface-treated strictly in accordance with international standards to ensure their reliability, wear resistance, and durability in complex downhole environments.